Lead-free free-cutting magnesium brass alloy and its manufacturing method

ABSTRACT

A lead-free free-cutting magnesium brass alloy comprises 56.0 to 64.0 wt % Cu, 0.6 to 2.5 wt % Mg, 0.15 to 0.4 wt % P and other elements 0.002 to 0.9 wt % which comprise at least two elements selected from the group consisting of Al, Si, Sb, Sn, Re, Ti and B and the balance being Zn and unavoidable impurities. The process for producing such alloy is also proposed. The invented alloy is excellent in cuttability, castability, hot and cold workability, corrosion resistance, mechanical properties and weldability and particularly applicable in spare parts, forging and castings which need cutting, grinding and electroplating process. The cost of necessary metal materials of the invented alloy is lower than lead-free free-cutting bismuth and antimony brass alloy and is equivalent to lead-contained brass alloy.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 12/207,136 filed on Sep. 9, 2008, which claims priority from Chinese Patent Application No. 200810110818.3 filed Jun. 11, 2008.

FIELD OF THE INVENTION

The present invention generally relates to a magnesium brass alloy, especially a lead-free free-cutting magnesium brass alloy which is applicable in spare parts for a water supply system.

BACKGROUND OF THE INVENTION

It is well-known that lead-containing brass alloys such as CuZn40Pb1, C36000, C3604 and C3771 usually contain 1.0-3.7 wt % Pb for ensuring excellent free-cuttability.

Lead-containing brass alloys are still widely used in the manufacture of many products due to their excellent cuttability and low cost. However, Pb-contaminated steam produced by the process of smelting and casting lead-contained brass alloy and Pb-contaminated dust produced in the process of cutting and grinding the lead-contained brass alloy are harmful to the human body and the environment. If the lead-containing brass alloys are used in drinking-water installations such as faucets, valves and bushings, contamination of the drinking water by Pb is unavoidable. In addition, toys which are produced by Pb-containing brass alloys are more harmful, as they are touched frequently, thus increasing potential exposure to Pb.

Ingestion of lead by humans is harmful, so the use of lead is being strictly banned by law in many countries due to the concerns on health and environment. For dealing with this challenge, metallurgists and manufacturers of copper materials actively research and develop lead-free free-cutting brass alloys. Some of them use Si instead of Pb, but the cuttability is not remarkably improved and the cost increases due to the high quantity of copper. Therefore, silicon brass alloys are not commercially competitive at present. One commonly used type of lead-free free-cutting brass alloy is a bismuth brass alloy, which uses bismuth instead of Pb. Many kinds of bismuth brass alloys with high or low zinc have been developed and their formal alloy grades have been registered in the United States. These kinds of brass alloy contain valuable tin, nickel and selenium as well as bismuth. Although their cuttability is 85%-97% of lead-contained brass alloy C36000, their cost is far higher than lead-contained brass alloy C36000. Therefore, these kinds of bismuth brass alloys are not competitively priced. Bismuth brass alloys also have been researched and developed in Japan and China and filed in their Patent Office. Considering that bismuth element is expensive, rare in the reserves and has poor cold and hot workability, using a bismuth brass alloy instead of a lead-containing brass alloy may be financially problematic. The invention of a free-cutting antimony brass alloy which use Sb instead of Pb has been patented in China (ZL200410015836.5). A corresponding U.S. (US2006/0289094) is currently pending.

DETAILED DESCRIPTION

One object of the present invention is to provide a magnesium brass alloy which will solve the limitations of conventional brass alloy discussed above especially the problem of lead contamination.

One object of the present invention is to provide a lead-free magnesium brass alloy which is excellent in cuttability, castability, hot and cold workability and corrosion resistance and not harmful for the environment and the human body.

One object of the present invention is to provide a lead-free free-cutting magnesium brass alloy which is particularly applicable in spare parts for water supply systems.

One object of the present invention is to provide a manufacturing method for a magnesium brass alloy.

The objects of the present invention are achieved as follows.

The present invention is intended to provide a lead-free free-cutting magnesium brass alloy which comprises: 56.0 to 64.0 wt % Cu, 0.6 to 2.5 wt % Mg, 0.15 to 0.4 wt % P, other elements 0.002 to 0.9 wt %, (the said other elements comprise at least two elements selected from among Al, Si, Sb, Sn, Re, Ti and B) and the balance being Zn and unavoidable impurities.

The invented alloy is in the base of alpha-beta brass and realizes excellent cuttability by the fracture of intermetallic compounds Cu₂Mg which is formed from element Mg and Cu.

In the present invention, P is an important element. It improves castability, weldability, dezincification, and corrosion resistance of the invented alloy. The intermetallic compounds Cu₃P which is formed from element P and Cu is complementary for the cuttability of the invented alloy. If the content of P is lower than 0.1 wt %, its benefit for cuttability of the magnesium brass alloy is not apparent. Therefore, the addition of P is preferably set in the range of 0.15 to 0.3 wt %, more preferably in the range of 0.2 to 0.29 wt % and most preferably in the range of 0.26 to 0.28 wt %.

The invented alloy presents multi-component alloying and grain refining which favors the intermetallic compounds Cu₂Mg and Cu₃P in granular form to uniformly disperse in the interior and boundary of the crystal grain and improves plasticity of the alloy.

The conventional brass alloy in the prior art usually contains a small amount of Mg (less than 0.01 wt %) for deoxidization and grain refining, contains a small amount of P (among 0.003 to 0.006 wt %) for deoxidization or for improving weldability of the brass alloy. In the present invention, the content of Mg and P is much higher than the prior art discussed above. The invented alloy has excellent integrated performance. The invented alloy actually is a kind of new lead-free magnesium brass alloy with a high level of P.

Mg is one of the main elements of the invented alloy except for Zn. At 722° C., the solid solubility of Mg in the matrix of copper is 3.3 wt %. The solid solubility of Mg in the matrix of copper will be decreased rapidly with the temperature decrease. The solid solubility will be equivalent to zero when the temperature is equivalent to the room temperature, precipitated Mg with Cu will form brittle but not hard intermetallic compounds Cu₂Mg. Considering this characteristic of Mg, Mg is selected as one of the main elements of the invented alloy for ensuring the cuttability of the invented alloy. Mg also has the effect of deoxidization, grain refining and dezincification corrosion resistance. However, with the increasing of Mg addition, the effects of dezincification corrosion resistance and castability will decrease. If the content of Mg exceeds 2.5 wt %, the effect of oxidization resistance of the invented alloy will decrease and the face of the ingot or castings will have a darker appearance. The addition of Mg is preferably set in the range of 0.5 to 2.0 wt % and more preferably in the range of 0.7 to 1.6 wt %.

Among other elements, Sb is a beneficial element for improving dezincification corrosion resistance. When Mg and P are contained in the invented alloy, the content of Sb is preferably set in the range of 0 to 0.25 wt %. Al, Si and Sn have the effects of deoxidization, solid solution strengthening and corrosion resistance. If the content of Al and Si is higher, the flowability of the alloy melt will decrease. If the content of Si is higher, hard and brittle γ-phase will form from Si and Cu so that the plasticity of the alloy melt will decrease. Preferably the addition of Al, Si and Sn is separately set in the range of 0.1 to 0.4 wt %. Re, Ti and B are very effective in grain refinement. Most kinds of lead-free free-cutting brass alloy more or less comprise these elements. The invented alloy also contains one or two such elements for grain refinement. Re also could ease the intermetallic compounds to disperse in the boundary of crystal grain and partially transfer to the interior of crystal grain.

Fe also could refine the crystal grains for brass alloy, but Fe without solution or precipitated Fe as temperature decreases will influence the corrosion resistance of the alloy and consume P which is an important element for the invented alloy. The amount of Fe as an unavoidable impurity in the invented alloy is less than 0.05 wt %. The amount of Pb as an unavoidable impurity in the invented alloy is less than 0.02 wt %.

The cost of necessary metal materials of the invented alloy is lower than lead-free free-cutting bismuth brass alloy and antimony brass alloy and is equivalent to lead-contained brass alloy by election of alloy elements and design of element content.

The manufacturing processing of the invented alloy is as follows:

The raw materials used in the alloy in accordance with the invention include: electrolytic Cu, electrolytic Zn, brass scrap, magnesium alloy, Cu—P master alloy, Cu—Si master alloy, Cu—Ti master alloy, Cu—B master alloy, and optionally industrially pure Sb, Al, and Re. The raw materials are added in a non-vacuum intermediate frequency induction electric furnace with a quartz sand furnace lining, in the following order:

First, electrolytic Cu, brass scraps, and covering agent that enhances slag removal efficiency are added to the furnace. These materials are heated until they have melted. Then the Cu—Si master alloy, Cu—Ti master alloy, and Cu—B master alloy are added to the melt. Thereafter, pure Sb, Sn, Al and Re may optionally be added. These materials are again heated until melted, and are thereafter stirred. Then electrolytic Zn is added to the melt. The melt is stirred, and slag is skimmed from the melt. The Cu—P master alloy is then added, and the melt is stirred further. At last the magnesium alloy is added, and the melt is stirred further. When the melt reaches a temperature of 995 to 1030 degrees Celsius, it is poured into ingot molds.

The alloy ingots may be processed in different ways according to the method of the invention. First, the ingot may be extruded at a temperature among 550 to 720 degrees Celsius for about 1 hour with an elongation coefficient of greater than 30 to be formed, for example, into bar. Second, the ingot may be die forged at a temperature among 580 to 680 degrees Celsius to be formed, for example, into a valve body, or for manufacturing other water supply system components. Third, the ingot may be remelted and cast at a temperature among 995 to 1015 degrees Celsius at a pressure of 0.3 to 0.5 Mpa for manufacturing faucets.

The advantages of the invented alloy are as follows. Smelting is processing in the atmosphere when the metals are protected with the covering agent. The addition of easily oxidized and volatile Mg is not effected by the addition of a conventional Cu—Mg master alloy or pure magnesium, but rather by Mg-based alloy whose melting point is lower than pure magnesium and boiling point is higher than pure magnesium. This reduces the consumption of Mg and is better to control the addition of Mg. Casting ingots rather than extruding bars are used to disposably form spare parts with complex structures for water supply systems by precision die forging. It could take out extruding process and save manufacturing cost. By die forging and extruding with an elongation coefficient greater than 30, the intermetallic compounds Cu₂Mg and grain are further refined and dispersed uniformly thereby improving the mechanical properties of the invented alloy. The manufacturing method of the invented alloy is easy to carry out. And the equipments for production are the same as Pb-contained brass alloy.

BRIEF DESCRIPTION OF THE DRAWINGS

To understand the present invention, it will now be described by way of example, with reference to the accompanying drawings in which:

FIG. 1 shows the shapes of the cutting chips formed in Examples 1, 2 and 3.

FIG. 2 shows the shapes of the cutting chips formed in Examples 4, 5 and 6.

FIG. 3 shows the shapes of the cutting chips formed in Examples 7, 8 and 9.

FIG. 4 shows the shapes of the cutting chips formed in cutting lead-contained brass alloy C36000 for comparison.

EXAMPLES

The alloy composition in examples is shown in Table 1. Some alloy ingot is extruded at the temperature ranging from 580° C. to 700° C. with an elongation coefficient of greater than 30 into bar materials. Some alloy ingot is forged at the temperature ranging from 590° C. to 710° C. to be spare parts with a complex structure for a water supply system. Some alloy ingot is remelted at the temperature among 990 to 1015° C. to make faucets by low pressure die casting.

TABLE 1 Composition of lead-free free-cutting magnesium brass alloy (wt %) Examples Cu Mg P Sb Si Al Sn Ti B Re Zn 1 59.25 0.58 0.29 0.21 0.38 0.20 <0.01 0.04 0.0004 — Balance 2 59.20 0.61 0.26 <0.03 0.40 0.21 0.25 0.03 0.0003 — Balance 3 58.63 0.70 0.28 0.25 0.36 0.17 0.20 0.003 0.0003 0.005 Balance 4 59.80 0.89 0.20 0.16 0.33 0.15 <0.02 0.03 0.0003 — Balance 5 59.76 0.94 0.15 0.11 0.35 0.10 <0.02 0.02 0.0002 — Balance 6 58.89 0.97 0.18 <0.03 0.31 0.20 <0.02 0.02 0.0002 — Balance 7 60.21 1.35 0.15 0.12 0.20 0.17 <0.03 0.01 0.0001 — Balance 8 60.40 1.60 0.19 0.14 0.23 0.15 <0.19 0.01 0.0001 — Balance 9 60.40 2.11 0.15 <0.03 0.16 0.10 0.22 0.01 0.0001 — Balance

The lead-free brass alloy of present invention has been tested with results as follows:

1. Cuttability Test:

The samples for testing are in the half-hard state. The same cutting tool, cutting speed and feeding quantity (0.6 mm) is approached. The relative cutting ratio is calculated by testing cutting resistance of alloy C36000 and the invented alloy:

$\frac{{Cutting}\mspace{14mu} {resistance}\mspace{14mu} {of}\mspace{14mu} {alloy}\mspace{14mu} C\; 36000}{{Cutting}\mspace{14mu} {resistance}\mspace{14mu} {of}\mspace{14mu} {the}\mspace{14mu} {invented}\mspace{14mu} {alloy}} \times 100\%$

It's assumed that the cutting ratio of alloy C36000 is 100%. FIG. 4 shows the shapes of the cutting chips formed in cutting lead-containing brass C36000. Then the cutting ratio of examples 1, 2 and 3 is ≧80% by testing the cutting resistance of alloy C36000 and examples 1, 2 and 3 of the invented alloy. FIG. 1 shows the shapes of the cutting chips formed in Examples 1, 2 and 3.The cutting ratio of examples 4, 5 and 6 is ≧85% by testing the cutting resistance of alloy C36000 and examples 4, 5 and 6 of the invented alloy. FIG. 2 shows the shapes of the cutting chips formed in Examples 4, 5 and 6. The cutting ratio of examples 7, 8 and 9 is ≧90% by testing the cutting resistance of alloy C36000 and examples 7, 8 and 9 of the invented alloy. FIG. 3 shows the shapes of the cutting chips formed in Examples 7, 8 and 9.

Dezincification Corrosion Test:

The test for dezincification corrosion resistance is conducted according to PRC national standard GB10119-88. The samples for testing are in the stress relief annealing state. The test results are shown in Table 2.

Stress Corrosion Test

The samples for test are from extruded bar, castings and forging. The test for stress corrosion is conducted according to PRC national standard GB/T10567.2-1997, Ammonia fumigation test. The test results are satisfactory when no crack appears in the face of the samples.

Mechanical Properties Test

The samples for testing are in the half-hard state. The specification is φ6 mm bar. The test results are shown in table 2.

Castability Test

Several indexes can be used to measure the castability of the alloy. The test for conventional volume shrinkage and spiral simples is for measuring the flowability of the alloy. The test for cylindrical samples is for measuring shrinkage crack resistance of the alloy. The test for strip samples is for measuring linear shrinkage rate of the alloy. For volume shrinkage samples, as may be seen in Table 2, if the face of the concentrating shrinkage cavity is smooth, and no visible shrinkage porosity in the bottom of the concentrating shrinkage cavity, it indicates castability is excellent and will be shown as “∘” in Table 2. If the face of the concentrating shrinkage cavity is smooth but the height of visible shrinkage porosity in the bottom of the concentrating shrinkage cavity is less than 5 mm, it indicates castability is good, and will be shown as “Δ” in Table 2. If the face of the concentrating shrinkage cavity is not smooth and the height of visible shrinkage porosity in the bottom of the concentrating shrinkage cavity is more than 5 mm, it indicates castability is poor, and will be shown as “×” in Table 2. For strip samples, the linear shrinkage rate is not more than 1.5%.For cylindrical samples, as may be seen in Table 2, if no visible shrinkage crack is shown, it indicates castability is excellent and will be shown as “∘” in Table 2. If the visible shrinkage crack is shown, it indicates the castability is poor, and will be shown as “×” in Table 2. Spiral samples are for measuring the flowability of the invented alloy. The test results of castability are shown in Table 2. The above results indicate the castability of the alloy is fine.

TABLE 2 Dezincification corrosion, mechanical properties and castability of the invented alloy Examples 1 2 3 4 5 6 7 8 9 C36000 Dezincification layer 90 110 95 100 120 120 150 230 320 610 depth/μm Mechanical Tensile 490 495 505 520 520 510 500 515 485 485 Properties strength/MPa 0.2% Yield 350 340 360 380 380 360 375 350 340 340 strength/MPa Elongation/% 13  14  12  12  11  12 10.6  10 9.5  9 Castability Concentrating ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ □ ∘ shrinkage cavity Shrinkage ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ crack Melt fluid 515 504 495 480 485 480 470 430 400 470 length/mm Linear 1.35~1.71 1.95~2.15 shrinkage rate/% 

1. A lead-free free-cutting magnesium brass alloy comprising: 56.0 to 64.0 wt % Cu, 0.6 to 2.5 wt % Mg, 0.20 to 0.4 wt % P, and other elements 0.002 to 0.9 wt % which comprise at least two elements selected from the group consisting of Al, Si, Sb, Sn, Re, Ti and B and the balance being Zn and unavoidable impurities.
 2. The lead-free free-cutting magnesium brass alloy of claim 1 wherein the content of P is between 0.20 to 0.3 wt %.
 3. The lead-free free-cutting magnesium brass alloy of claim 2 wherein the content of P is between 0.2 to 0.29 wt %.
 4. The lead-free free-cutting magnesium brass alloy of claim 1 wherein the content of Mg is between 1.0 to 2.0 wt %.
 5. The lead-free free-cutting magnesium brass alloy of claim 4 wherein the content of Mg is between 1.0 to 1.6 wt %.
 6. (canceled)
 7. The lead-free free-cutting magnesium brass alloy of claim 5, wherein other elements are selected from Ti and B.
 8. The lead-free free-cutting magnesium brass alloy of claim 1 wherein the content of other elements is between 0.003 to 0.8 wt %.
 9. The lead-free free-cutting magnesium brass alloy of claim 7 wherein the content of other elements is between 0.003 to 0.05 wt %.
 10. (canceled) 11-14. (canceled)
 15. The lead-free free-cutting magnesium brass alloy of claim 1 wherein the cutting ratio percentage of said alloy is at least 85%.
 16. The lead-free free-cutting magnesium brass alloy of claim 1 wherein the cutting ratio percentage of said alloy is at least 90%. 